Powder Metallurgy Tungsten Alloy Rod and Machinery Parts

• After-sales Service: a Full Two-Year Warranty
• Warranty: Two-Year Warranty
• Condition: New
• Certification: RoHS, ISO9001
• Standard: ASTM
• Customized: Customized
• Model NO.: Special shaped products of Tungsten alloy
• Material: Tungsten Alloy
• Application: Metal Processing Machinery Parts
• Composition: 90%-97%Wnife or 90%-97%Wnicu
• Supply State: Sintered, Forged and Vacuum Treatmen
• Quality: ISO9001:2015 Accredited
• Grade: ASTM-B-777 Class 1, 2, 3, and 4, Mil-T-21014, AMS-
• Nominal % Tungsten: 90t92.5t 95t 97
• Nominal Density G/Cc: 16.85~17.30 17.15~17.85 17.75~18.35 18.25~18.85
• Mini Ultimate Tensile Strength MPa: 758 758 724 689
• Mini Yield Strength MPa: 517 517 517 517
• Mini Elongation %: 5 5 3 2
• Magnetism: Magnetic, Non-Magnetic
• Transport Package: Export Wooden Case
• Specification: Dia (3-400) mm X L (20-1200) mm or customized
• Trademark: Kefeng
• Origin: China
• HS Code: 81019990

Product Description

Xi'an Kefeng Powder Metallurgy Co., Ltd, As a Chinese manufacturer, combines producing tungsten alloy material and machining complex drawing products with high precision tungsten heavy metal products.
Main products:
1) Tungsten Based high density alloy:  Meet ASTM B777 standard and ASTM B7725 standard.
A) (90-97)%W+Ni+Fealloy, Magnetic, density: 16.85-18.75g/cc. Hardness: 34HRC max. UTS, YS and EL, see below table.
B) (90-97)%W+Ni+Cu alloy, Non-Magnetic,  density 16.85-18.75g/cc. Hardness: 34HRC max. UTS, YS and EL, see below table.

2) Copper-Tungsten alloy,  (70-85)% Tungsten + Copper balance.  Meet ASTM B702 standard.
3) Pure Molybdenum: We can supply pure Molybdenum, Mo-La, TZM molybdenum. Meet ASTM B386 and ASTM B387 standards.
4) Pure Tungsten: We also can supply pure tungsten, 99.95%W, density:19.3g/cc., As per ASTM B760 Standard.

Technical parameters
 

Tungsten heavy alloy	WNiFe (ASTM B777, AMS-T-21014)				WNiCu (ASTM B777, AMS-T-21014)
Designation	90W	93W	95W	97W	90W	93W	95W
Density g/cm3)	16.85~17.30	17.15~17.85	17.75~18.35	18.25~18.85	16.85~17.30	17.15~17.85	17.75~18.35
Tensile Strength (MPa)	758Min	758Min	724Min	689Min	648Min	648Min	648Min
Elongation (%)	5Min	5Min	3Min	2Min	2Min	2Min	1Min
Hardness (HRC)	32Max	33Max	34Max	35Max	32Max	33Max	34Max
Yield strength(MPa)	517Min	517Min	517Min	517Min	517Min	517Min	517Min