China Reliable Powder Metallurgy Aerospace Parts Tungsten Bucking Bars

• Customization: Available
• Application: Aviation, Electronics, Industrial, Medical, Chemical, Aerospace
• Standard: GB, ASTM
• Model NO.: TB004
• Purity: 90%~97%
• Alloy: Alloy
• Shape: Various Sizes or According to Drawings
• Type: Rods
• Supply State: Sintered, Forged and Vacuum Treatment
• Customized: Sheet/Plate/Foil/Strip According to Drawi
• Material: 90%-97%Wnife or 90%-97%Wnicu
• Grade: ASTM B777-15 AMS 7725 Mil-T-21014
• Density: 16.85~17.30g/Cc, 17.15~17.85g/Cc, 18.25~18.85g/Cc
• Ultimate Tensile Strength: 758MPa, 724MPa, 689MPa
• Class: 1, 2, 3, 4
• Yield Strength: 517MPa
• Elongation: 5%, 3%, 2%
• Nonmagnetic Alloys: Ultimate Strength 648MPa, 648MPa, Na
• Nonmagnetic Yield Strength: 517MPa, Na
• Nonmagnetic Elongation: 2%, 1%, Na
• Processing 1: Expert Set
• Rrocessing 2: Notched and Angeled Set
• Transport Package: Export Wooden Box with Foam Inside
• Specification: Standard sizes or customized
• Trademark: Kefeng
• Origin: China
• HS Code: 81019910

Product Description

Product Description

Kefeng's Tungsten bucking bars provide increased weight (density) to allow riveting in confined areas. The weight to size ratio provides a good kinetic energy transfer to expedite the rivet installation process. Our Tungsten bucking bars greatly reduce the vibration caused by driving rivets reducing or eliminating damage to the hand. They are precision ground with polished surface fora professional look in your set rivets.  Kefeng tungsten bucking bars are available in standard sizes and shapes customized or clients drawings.

China Reliable Powder Metallurgy Aerospace Parts Tungsten Bucking Bars reduce vibration and kickback while riveting in aircraft operations. Repeated vibrations can cause wrist strain and fatigue, and regular steel bucking bars don't fully protect the riveter from the harmful effects. Tungsten material bucking bars, over twice as dense as normal steel, absorbs the shock, allowing you to rivet more effectively for a longer period of time.

Characteristics and features

Tungsten alloy offer the maximum density available, these tungsten alloy bars are more than twice as heavy as an identical bar made of steel, small size and high density make the bars can fit small areas.
Small size and same weight ,tungsten alloy bucking bars reduce the recoil when reflecting the impact back to the rivet shaft. Bars that are more massive can reduce vibration transmitted to the hand. Tungsten alloy bucking bar makes any riveting process much easier, provide a good kinetic energy transfer to expedite the rivet installation process thus can greatly reduce the vibration caused by driving rivets and eliminate damage to operators' hands.

1. High temperature resistance
2. High impact and crack resistance
3. Shock and corrosion resistance
4. Good modulus of elasticity and high hardness

China Reliable Powder Metallurgy Aerospace Parts Tungsten Bucking Bars range from 16.5-19.0 g/cm3 density of tungsten heavy alloys WNiFe and WNiCu are the most important industrial property. The density of tungsten is two times higher than steel and 1.5 times higher than lead. Although many other metals such as gold, platinum, and tantalum, have a comparable density to heavy tungsten alloy, they are either over expensive to obtain or exotic to the environment. Combined with the high machinability and high module elasticity, the density property makes the tungsten heavy alloy to be capable of being machined into a variety of density needed components in many industrial fields. Given an example of counterweight. In a very limited space, a counterweight made of both materials are the most preferred material to offset the gravity change caused by off-balance, vibration, and swinging.

Application

China Reliable Powder Metallurgy Aerospace Parts Tungsten Bucking Bars are mostly used in aviation, aerospace and aircraft industries.  Other applications for tungsten heavy alloy machining parts:

1. Balance Weights
2. Aircraft Ballast Weights
3. Rotor Bldes
4. Propellers
5. Rudders
6. Magnets
7. Electrodes
8. Vibration Dampening Parts
9. Missile Components
10. Thermal Management Applications
11. Jet Engines
12. Heat Resistant Equipment
13. Nozzles
14. Aircraft Parts
15. Rocket Engines 

Detailed Photos

Product Parameters

Powder Metallurgy Aerospace Parts Tungsten Bucking Bars

Tungsten heavy alloy	WNiFe (ASTM B777, AMS-T-21014)				WNiCu (ASTM B777, AMS-T-21014)
Designation	90W	93W	95W	97W	90W	93W	95W
Density g/cm3)	16.85~17.30	17.15~17.85	17.75~18.35	18.25~18.85	16.85~17.30	17.15~17.85	17.75~18.35
Tensile Strength (MPa)	758Min	758Min	724Min	689Min	648Min	648Min	648Min
Elongation (%)	5Min	5Min	3Min	2Min	2Min	2Min	1Min
Hardness (HRC)	32Max	33Max	34Max	35Max	32Max	33Max	34Max
Yield strength(MPa)	517Min	517Min	517Min	517Min	517Min	517Min	517Min

Our Quality Assurance


Our Test Equipment

We offer the test report including all relevant technical data for the properties of physical, material, chemical ects for all finished products.